Sealmax Style 9006
Sealmax Style 9006 is manufactured from mineral fiber, cellulose fiber, organic fiber, inorganic fillers and NBR binder.
Style 9006 is suitable for low operating pressure applications such as transformers and compressors. It is also recommended for easily deformable components with low surface pressure, such as valve covers and pans in internal combustion engines.
(Refer to pressure–temperature graph)
- Gasket material is normally suitable, subject to chemical compatibility.
- Gasket material may be suitable; technical support is recommended.
- Do not install the gasket without technical evaluation.
Technical Specifications (All data are typical values and refer to a sheet thickness of 2.0 mm) | ||||
SR.NO. | PROPERTIES | Test Method | Specified Value | Unit |
1. | Max. Peak Temperature | – | 200 | °C |
2. | Max. Operating Temperature | – | 165 | °C |
3. | Max. Operating Pressure | – | 50 | bar |
4. | Density | ASTM F 1315 | 1.60 – 1.90 | g/cm³ |
5. | Compressibility | ASTM F 36 J | 7 – 17 | % |
6. | Recovery | ASTM F 36 J | ≥ 40 | % |
7. | Tensile Strength | ASTM F 152 | ≥ 7 | N/mm² |
8. | Gas Permeability | BS 7531 | ≤ 1.0 | ml/min |
9. | ASTM Oil No. 3 (5h, 150°C) | ASTM F 146 |
|
|
9a. | Thickness Increase |
| ≤ 15 | % |
9b. | Weight Increase | ≤ 20 | % | |
10. | Fuel B (5h, 23°C) | ASTM F146 |
|
|
10a. | Thickness Increase |
| ≤ 20 | % |
10b. | Weight Increase | ≤ 20 | % | |
11. | Water (5h, 100°C) | ASTM F 146 |
|
|
11a. | Thickness Increase |
| ≤ 10 | % |
11b. | Weight Increase |
| ≤ 15 | % |
12. | Stress Relaxation (16h x 175°C) | DIN 52913 | ≥ 15 | MPa |
General Specifications | ||
SR.NO. | Particulars | Remarks |
1. | Standard Sheet Size | 1500 mm x 1500 mm, 1500 mm x 2000 mm, 1500 mm x 3000 mm, 1500 mm x 4000 mm, 1500 mm x 4500 mm, 2000 mm x 3000 mm |
2. | Standard Thickness | 0.40 mm to 6.0 mm |
3. | Tolerance on Width | ± 50 mm |
4. | Tolerance on Length | ± 50 mm |
5. | Tolerance on Thickness | < 1mm = ± 0.10mm> 1 mm = ± 10% |